Fracture strength of telescopic zirconia secondary crowns of different taper and thickness
https://osaka-dent.repo.nii.ac.jp/records/297
https://osaka-dent.repo.nii.ac.jp/records/2975aa40f61-75e2-484b-b83d-db4a538da776
名前 / ファイル | ライセンス | アクション |
---|---|---|
![]() |
|
|
![]() |
|
Item type | 学位論文 / Thesis or Dissertation(1) | |||||||||||
---|---|---|---|---|---|---|---|---|---|---|---|---|
公開日 | 2021-04-23 | |||||||||||
本文言語 | ||||||||||||
言語 | eng | |||||||||||
タイトル | ||||||||||||
タイトル | Fracture strength of telescopic zirconia secondary crowns of different taper and thickness | |||||||||||
著者 |
柴田, 駿亮
× 柴田, 駿亮
× Shibata, Shunsuke
|
|||||||||||
キーワード | ||||||||||||
主題Scheme | Other | |||||||||||
主題 | Telescopic crowns|Y-TZP| Zirconia| Fracture strength | |||||||||||
資源タイプ | ||||||||||||
資源タイプ識別子 | http://purl.org/coar/resource_type/c_db06 | |||||||||||
資源タイプ | doctoral thesis | |||||||||||
アクセス権 | ||||||||||||
アクセス権 | open access | |||||||||||
アクセス権URI | http://purl.org/coar/access_right/c_abf2 | |||||||||||
抄録 | ||||||||||||
内容記述タイプ | Abstract | |||||||||||
内容記述 | The objective of this study was to clarify the influence of the half taper angle and thickness of the zirconia secondary crown on its fracture strength. Y-TZP was used for both primary and secondary crown. Samples were prepared at the half taper angles of 2° and 4° and a secondary crown thickness of 0.5 and 1.0 mm (n=7). The secondary crown was restored on the primary crown and the fracture strength was determined by loading all specimens until fracture using a universal testing machine. The load applied at the time of secondary crown fracture was regarded as fracture strength. Based on the analysis of variance, although the fracture strength at 1.0-mm thickness was significantly greater than that at 0.5-mm thickness, the taper angle had no influence on the fracture strength. | |||||||||||
学位名 | ||||||||||||
学位名 | 博士(歯学) | |||||||||||
学位授与機関 | ||||||||||||
学位授与機関識別子Scheme | kakenhi | |||||||||||
学位授与機関識別子 | 34408 | |||||||||||
学位授与機関名 | 大阪歯科大学 | |||||||||||
学位授与年月日 | ||||||||||||
学位授与年月日 | 2021-03-05 | |||||||||||
学位授与番号 | ||||||||||||
学位授与番号 | 甲第910号 |